         Unsaturated Polyester Resins
  General Purpose (G.P.)
  Isopthallic Resin (ISO Resin)
  Rooflight (Sheet)
  Flame Retardant (FR) Resin
  Gelcoat GP
  Gelcoat ISO
  Gelcoat Acralic
         Chopped Strand Mat
  Powder Bonded
  Emulsion Bonded
  Woven Roving (W/R)
  Surface Mat
         M.E.K.P. ( CATALYST)

"A substance added to a polyester in a certain quantity to allow the polyester to cure (Harden). Peroxides are the catalysts used with polyester"

         COBALT (Accelerator)

"A high active oxidizing material suspended in a liquid carrier used to accelerate the decomposition of peroxide catalysts into highly reactive free radicals. These free radicals react readily With polymer and monomer molecules to cure a thermoset resin."

         PVA POWDER
  General Purpose Resin (G.P.)

We are trader of the general purpose unsaturated polyester resin that is widely used in chemical equipment, industrial purpose, marine industry, auto industry and FRP cooler bodies. These are developed with innovative technique of production to ensure international quality standards. We compiles with requirements of companies interested in improved efficiency and superior performance of their finished product.


Automobile Components
Flower pot
Sports Equipments
Safety Helmet
Dust Bin
Water Tank
Garden Furniture
Bath Tub
Machine Cover


The general purpose polyester resin is a quick curing unsaturated polyester resin based on Orthophthalic raw material for laminating purpose. It is un-accelerated. Suitable for both hand lay up and gun spray up. The resin offers excellent mechanical properties, impact and water resistance. The glassfibre laminate made with this resin has excellent mechanical strength, good rigidity and outstanding durability.

Muddy yellow & clear transparent in color
Medium reactivity
Good water resistance
Efficient heat resistance


The general purpose polyster resins performs best if the laminate is completely post cured. The quantity of catalyst and accelerator can be adjusted to get a shorter or longer gel time. The accelerator must be completely mixed before catalyst is added in order to avoid a direct blending which may cause an explosion.
It is recommended to mature the products for 24 hours and post curing should be done for minimum of three hours at 800C, or 2-3 weeks at room temperature. This is essential for getting the optimum properties.


The polyester resin remains stable for 3 months at 300C in the dark and 4 months at 250C. The resin stability deteriorates markedly at elevated temperature, especially when exposed to direct sunlight. "NO SMOKING " rules should be strictly followed. In case of spillage, use sand or earth to absorb and shovel off for disposal as per local regulations, In case of fire, use dry chemical foam, Carbon dioxide or water spray to extinguish the flame.
The Polyester resin is packed in HDPE carboys ( 30, 35, 40 & 45 kgs ) and drums HDPE barrels ( 225 kgs ) of standard size net weight. Special packing size offered for projects on returnable containers. Technical services are also provided to comply standards.


Never add metal salts ( Accelerator ) or Pre Acceleratorated resin to Peroxides when adding peroxides to a resin solution, mix thoroughly the resulting product Do not add organic peroxides to a hot diluents or process. Prevent contamination of Accelerator, promoter from materials like ( Iron Copper, Cobalt ) salts, storing acids and sanding dusts. Suggested containers are glass, polypropylene, Teflon, Poly-ethylene or stainless steel to prevent contamination of material during its handling.

  For any related query please                                                                          

Regd. Off : F-60, Subhash Marg, C-Scheme, Jaipur-302001, Rajasthan (India)
:     S-8-A, Kartarpura Industrial Area, 22 Godown, Jaipur, Rajasthan (India)
:   +91-9829055935
:   +91-141-3239399  
:        +91-141-4027373
:  www.ananyafibrochem.com

  All Right Reserved@ Ananya Fibrochem Pvt. Ltd.